KYNAR - 2:1 SHRINK RATIO, HIGH TEMPERATURE CHEMICAL RESISTANT, PVF2 TUBING Applications A semi-rigid, flame retardant, heat shrinkable polyvinylidene fluoride (PVF2) tube for applications requiring outstanding abrasion and cut-through resistance. It reliably protects wires, solder joints, terminals, connections and components from most industrial fuels, solvents and chemicals. Features - Shrink ratio: 50% or more in the radial direction, 5% or less in the axial direction - Continuous operating temperature: - 55°C to 175°C - Flammability: UL VW-1, CSA OFT - Excellent electrical properties - High resistance to chemicals and oils Standard -UL 224 (File Number: E84393) - MIL-DTL-23053/8 Ordering Information / Product Dimensions Part # Spool Lengths Size Expanded Recovered Internal Diameter Minimum (D) Internal Diameter Maximum (d) Minimum Total Wall Thickness (t) Clear Ft. Inch Size In. mm In. mm In. mm M23053/8-001-SP 500' 3/64" 0.047 1.2 0.023 .0.58 0.007 0.180 M23053/8-002-SP 500' 1/16" 0.063 1.6 0.031 0.79 0.007 0.180 M23053/8-003-SP 500' 3/32" 0.094 2.4 0.046 1.17 0.010 0.250 M23053/8-004-SP 500' 1/8" 0.125 3.2 0.062 1.57 0.010 0.250 M23053/8-005-SP 250' 3/16" 0.188 4.8 0.093 2.36 0.010 0.250 M23053/8-006-SP 250' 1/4" 0.251 6.4 0.125 3.18 0.010 0.250 M23053/8-007-SP 200' 3/8" 0.377 9.6 0.187 4.75 0.011 0.279 M23053/8-008-SP 200' 1/2" 0.503 12.8 0.250 6.35 0.011 0.279 M23053/8-009-SP 100' 3/4" 0.759 19.3 0.370 9.35 0.014 0.356 M23053/8-010-SP 100' 1" 1.000 25.6 0.500 12.7 0.016 0.406 Specification Values Property Test Method Value Physical Unaged Tensile strength ASTM D 638 Min. 5,000 psi Elongation Min. 150% Aged Tensile strength 175°C/168 hrs Min. 70% of the value of unaged specimens Elongation Deformation 150°C/1 hr Max. 50% Heat shock 300°C/4 hrs No cracking, flowing or dripping Cold bend - 55°C/4 hrs No crack Flexibility 180°C/168 hrs No crack Secant Modulus 2% Strain Min. 120,000 psi Electrical Dielectric strength Room Temp Min. 23.6.kV/ mm Volume resistivity - Min. 10^13 Ω - cm Chemical Copper corrosion 180°C/168 hrs No corrosion Copper stability 180°C/168 hrs No sign of degradation Flammability VW-1 Pass